Aragonit Thermal Insulation Board Plaster-826
Product Code: A3020
Description: Cement-based polymer modified and added chemicals and high strength, durable movement is a thermal insulation board plaster.
Uses: applied to all kinds of interior and exterior plaster is used for thermal insulation plate.
Preparation: Application of surface roughness to be made, water absorption, stability is checked beforehand. Locations surface voids and repairs to be performed repairs done previously. The surface plaster dust, dirt, debris is cleaned from factors such as oil.
Mixing and Application: 6 - 7 liters. Clean water is discharged into the dust portion on the container and slowly added to the mixture and mixed until it becomes a homogeneous consistency. Low speed mixer is used to mix. To mix at a high speed prevents a homogeneous consistency. Wait 5 minutes after the maturation time is ready for use again stirred slurry. On Thermal Insulation Board with the help of prepared mixture of plaster trowels 2 or 3 mm. thickness is driven in. PVC mesh, properly adhered to the plaster. Plaster mesh and plate is secured to the substrate with the help of plastic anchors. This practice 2 hours after aragonite Thermal Insulation Board Plaster is applied with a trowel onto the net again and corrected the following floating. 24 hours after this application can be any dye or applications.
Application tools should be washed with water after application. On the application process can not be expired material and the surface must be cleaned. Hardened and used material in the vessel has completed the outlet.
Issues to be considered:
• The application surface of dust, dirt, spills should be cleaned of factors such as oil.
• Material must be mixed with a maximum of 120 speed mixer assistance.
• The mixture should be consumed within 2 hours.
• any contribution material outside material into the water (lime, sand, cement) should never be placed.
• should not be stacked more than 8 bags. Must be stored unopened in its original packaging stored in dry and dry.
• External factors (rain, sun, wind GB.) It is more durable than against the old plaster.
• the application and the application surface after application of external factors (wind, sun, moisture) must be protected.
• Application during protective equipment (clothing, gloves) should be used.
• Hand, eye and body contact should be avoided, wash immediately with plenty of water in contact with eyes, seek medical attention if necessary.
Binder: Cement-Based
Appearance: Powdered
Color: Gray
Mixing ratio: 25 kg product an average of 6 - 7 liters. admixed with water.
Amount of consumption: the average for 1 m2 4 - 4,5 kg.
Skinning Time: 60 minutes
Fresh mortar Hollow Unit Weight: ≥ 1150 kg / m3
Hardened Cement Based Plaster's Hollow Unit Weight: 1.57 ± 10% kg / m3
Sieve Analysis: 1 mm. screens at most 1%
Bending strength: ≥ 2.0 N / mm2
Compressive strength: ≥ 6.0 N / mm2
Thermal Insulation Board Adhesion: ≥ 0.08 N / mm2
Water Absorption: ≤ 0.5 (kg / m2.dakik 0.5)
Water Vapor Permeability Coefficient: ʮ ≤ 15
Thermal Conductivity: EN 1745 TABLE A.12 BY P: 50% (λ10, dry) 0.47 W / mK
Reaction to fire: A1 <1%
Packaging: 25 kg. (3 times in kraft bags, as Stretching)
Shelf life: dry and moisture environment as the production date is 1 year.
Storage: Store in dry and humid conditions with unopened package stored stacked on top of more than 8.
Ripening time: 5 minutes
Potlife: Depending on the ambient conditions can be used after mixing for 2 hours.
The Tests Below Have been Applied In The Scope of ETAG 004 Component Testing
• Water accumulation
• Static Tensile modules of elasticity
• Render strip tensile testing of the base coat
(* Stress at rupture * Elongation at rupture * Static modulus of elasticity)
• Bulk Density
• Ash Content
• Particle size grading
• Density of fresh mortar
• Density of hardened base coat